Calcium tungstate (CaWO4) crystals were prepared by microwave-assisted hydrothermal (MAH) and polymeric precursor methods (PPM). These crystals were structurally characterized by X-ray diffraction (XRD), N2 adsorption, X-ray absorption near edge spectroscopy (XANES) and extended X-ray absorption fine structure (EXAFS) measurements. The morphology and size of these crystals were observed by field emission scanning electron microscopy (FE-SEM). Their optical properties were investigated by ultraviolet visible (UV-Vis) absorption and photoluminescence (PL) measurements. Moreover, these materials were employed as catalysts towards gas phase toluene oxidation reaction. XRD indicates the purity of materials for both preparation methods and MAH process produced crystalline powders synthesized at lower temperatures and shorter processing time compared to the ones prepared by PPM. FE-SEM images showed particles with rounded morphology and particles in clusters dumbbells-like shaped. PL spectra exhibit a broad band covering the visible electromagnetic spectrum in the range of 360 to 750 nm. XANES and EXAFS results show that preparation method does not introduce high disorders into the structure, however the H2-TPR results indicated that the catalyst reducibility is affected by the preparation method of the samples.

In this study, electric arc furnace dust (EAFD) was thermally modified at different temperatures under H2 flow or charcoal in order to obtain reduced iron phases (Fe3O4, FeO and Fe0). The formation of these phases was confirmed by powder X-ray diffraction. The tests performed for reducing Cr (VI) using resultant materials obtained after thermal treatment of the EAFD showed excellent results, with PAE600H (EAFD reduced at 600 ºC under H2 flow) decreasing around 100% of the Cr (VI) in only 10 minutes of reaction. These results indicate the possibility of adding value to the residue, obtaining materials that offer great potential for environmental applications.